At a certain fracture toughness value, fracture probability of weldments increases with increase of the local brittle zone size.
在一定的断裂韧度前提下,随着局部脆性区尺寸的增加,焊接热影响区的脆断概率增加。
The research results showed that the slab surface temperature dropping into the third brittle zone played an important role in causing transverse crack formation ofm...
研究表明,铸坯表面温度落入钢的第三次脆性温度区是造成铸坯表面横裂的一个重要原因。
The research results showed that the slab surface temperature dropping into the third brittle zone played an important role in causing transverse crack formation of microalloyed slab.
研究表明,铸坯表面温度落入钢的第三次脆性温度区是造成铸坯表面横裂的一个重要原因。